ASTM D Standard Test Method for Ball-Pan Hardness of Activated Carbon. Standard Test Method for Ball-Pan Hardness of Activated Carbon. Status: Withdrawn · Replaced by: ASTM D Buy this standard. Price: SEK. PDF. D()活性碳的球盘硬度的试验方法 – Designation: D Referenced Documents ASTM Standards: B 19 Speci?cation for.

Author: Gunos Brasar
Country: Sierra Leone
Language: English (Spanish)
Genre: Environment
Published (Last): 2 April 2011
Pages: 374
PDF File Size: 4.4 Mb
ePub File Size: 11.16 Mb
ISBN: 246-2-81452-651-7
Downloads: 86188
Price: Free* [*Free Regsitration Required]
Uploader: Akinokus

If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below. Discard the fractions above the larger and below the smaller nominal particle size. Humidity effects during a given test will largely cancel out if no change in humidity occurs between 9.

Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. Adjust the bottom stops to give a clearance of approximately 1. Summary of Test Method 4.

A number in parentheses indicates the year of last reapproval. Your comments are invited either xstm revision of this standard or for additional standards and should be addressed to ASTM Headquarters.

Standard Test Method for Ball-Pan Hardness of Activated Carbon

Shake with the hammer operating for 10 min 6 10 s. Conceding the fact that the test does not actually measure in-service resistance to degradation, it can be used to establish the comparability of lots ostensibly of the same grade of carbon.

  DIE BESTEN AKTIENSTRATEGIEN PDF

Users of asstm standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility.

It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. One supplier tested 31 samples of a single grade of asttm and obtained an average hardness of Precision and Bias BoxGastonia, NChas been found to be satisfactory.

At the end of this period, the amount of particle size degradation is determined by measuring the quantity of carbon, by weight, which is retained on a sieve whose openings are closest to one half the openings of the sieve that de? Fit the cover plate with a cork stopper which extends from 3. This standard is subject to revision at any time by the responsible technical committee and must be reviewed every?

Weigh to the nearest 0. Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at the above address or at phonefaxor service astm.

  KAMAGNI FULL STORY PDF

Table 1 lists qstm hardness test sieve corresponding to each minimum nominal sieve. Obtain at least mL of material within the nominal mesh size range. The extra sieves, in this case, serve only to form a stack which? The value of H2 gives the upper limit of hardness, if we ignore the effects of humidity.

Apparatus and Materials 6.

Standard Test Method for Ball-Pan Hardness of Activated Carbon – CERN Document Server

None of these has proved completely satisfactory for all applications, and all have been questioned by ASTM Committee D on Activated Carbon as tests for establishing degradation resistance. Place the hardness test sieve on top of the receiving pan. Use additional material obtained as in 9. Pour the screened and weighed sample into the hardness pan and add the steel balls.

Sieves shall be calibrated at reasonable intervals in accordance with the procedure described in Speci? Tyler Model SB, available from W. A superscript epsilon e indicates an editorial change since the last revision or reapproval. The adhesion of material to sieves, brushes, etc.

Current edition approved June 29,